Microscopic origins of the induced X<sup>(2)</sup>in thermally poled phosphate glasses

We have investigated the microscopic origins of the induced X(2)in two phosphate glasses: a self-prepared lanthanum phosphate glass with molar composition 0.2La2O30.8P2O5and a commercial sodium alumino phosphate glass (IOG-1, Schott Glass Technologies, Inc.) with molar composition 0.6 P2O50.24Na2O 0...

全面介紹

Saved in:
書目詳細資料
Main Authors: P. Thamboon, D. M. Krol
格式: 雜誌
出版: 2018
主題:
在線閱讀:https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=67649529142&origin=inward
http://cmuir.cmu.ac.th/jspui/handle/6653943832/49451
標簽: 添加標簽
沒有標簽, 成為第一個標記此記錄!
實物特徵
總結:We have investigated the microscopic origins of the induced X(2)in two phosphate glasses: a self-prepared lanthanum phosphate glass with molar composition 0.2La2O30.8P2O5and a commercial sodium alumino phosphate glass (IOG-1, Schott Glass Technologies, Inc.) with molar composition 0.6 P2O50.24Na2O 0.13 Al2O3 0.03Ce2O3. The drastic difference in alkali content in these two phosphate glass systems results in different origins of their induced X(2). For the poled lanthanum phosphate glass, the origin of the induced X(2), which is directly proportional to the dc field established inside the glass, is the result of charge migration. A model that uses a single-positive-charge carrier with a nonblocking cathode describes the anodic surface X(2)of 30 μm thickness. For the poled sodium alumino phosphate glass, two mechanisms-dipole reorientation via the applied field and charge migration-are responsible for the origin of the bulk and the surface X(2). Dipole reorientation via the applied field is suggested for the bulk contribution, while a charge migration model that involves multiple-charge carriers with nonblocking electrodes is appropriate for the surface X(2). © 2009 American Institute of Physics.