Effect of compressive stress on the ferroelectric hysteresis behavior in 0-3 PMN-PT/cement composites
Lead magnesium niobate titanate (PMN-PT)Portland cement (PC) composites were produced. PMN- PT amount used in this work were 30, 50, and 70% by volume. The effects of PMN-PT content (using 30%, 50%, 70% PMN-PT) and stress on the ferroelectric polarization-electric field (P-E) hysteresis of the compo...
Saved in:
| Main Authors: | , , |
|---|---|
| Format: | Journal |
| Published: |
2018
|
| Subjects: | |
| Online Access: | https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=79959366387&origin=inward http://cmuir.cmu.ac.th/jspui/handle/6653943832/50103 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Institution: | Chiang Mai University |
| Summary: | Lead magnesium niobate titanate (PMN-PT)Portland cement (PC) composites were produced. PMN- PT amount used in this work were 30, 50, and 70% by volume. The effects of PMN-PT content (using 30%, 50%, 70% PMN-PT) and stress on the ferroelectric polarization-electric field (P-E) hysteresis of the composites are reported in this present work. From the results, it was found that there was an increase in the instantaneous remnant polarization (Pir) when PMN- PT amount increased while Pirwas found to decrease when the stress was increased from 0 to 57 MPa. Copyright © Taylor & Francis Group, LLC. |
|---|