Crystal structure, thermal and magnetic behavior of inorganic-organic hybrid [VIV4O10 VV2O4] (C6H14N2) •H2O polymeric framework
The inorganic-organic hybrid [VIV4O 10VV2O4] (C6H 14N2)•H2O polymeric framework was prepared under mild hydrothermal conditions from a mixture of DABCO and V 2O5 in deionized water with a 1:1:450 mole ratio, at neutral pH. The reaction was carried out at 180°C for 3 days under autogenous pressure yi...
Saved in:
Main Authors: | , , , , |
---|---|
Format: | Article |
Language: | English |
Published: |
2014
|
Online Access: | http://www.scopus.com/inward/record.url?eid=2-s2.0-33750982096&partnerID=40&md5=6b70e1174abecdceae89cd3954d766ff http://cmuir.cmu.ac.th/handle/6653943832/5083 |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Institution: | Chiang Mai University |
Language: | English |
id |
th-cmuir.6653943832-5083 |
---|---|
record_format |
dspace |
spelling |
th-cmuir.6653943832-50832014-08-30T02:56:08Z Crystal structure, thermal and magnetic behavior of inorganic-organic hybrid [VIV4O10 VV2O4] (C6H14N2) •H2O polymeric framework Settheeworrarit T. Pakawatchai C. Maensiri S. Limtrakul J. Rujiwatra A. The inorganic-organic hybrid [VIV4O 10VV2O4] (C6H 14N2)•H2O polymeric framework was prepared under mild hydrothermal conditions from a mixture of DABCO and V 2O5 in deionized water with a 1:1:450 mole ratio, at neutral pH. The reaction was carried out at 180°C for 3 days under autogenous pressure yielding phase pure crystals product. The crystal structure was studied using both powder and single crystal X-ray crystallography, revealing the structure to be of the ({UuDd}:T*)α′ type in the SP+T class and Z-T subclass. The presence of the organic cation was confirmed by FT-IR spectrum and chemical composition analysis. The structure was thermally stable up to over 400°C, and showed ferromagnetic character at room temperature with the maximum molar susceptibility of 8.26 × 10 -3 emu/mol-1 at zero applied field. © 2006 Springer Science+Business Media, LLC. 2014-08-30T02:56:08Z 2014-08-30T02:56:08Z 2006 Article 15741443 10.1007/s10904-006-9051-x http://www.scopus.com/inward/record.url?eid=2-s2.0-33750982096&partnerID=40&md5=6b70e1174abecdceae89cd3954d766ff http://cmuir.cmu.ac.th/handle/6653943832/5083 English |
institution |
Chiang Mai University |
building |
Chiang Mai University Library |
country |
Thailand |
collection |
CMU Intellectual Repository |
language |
English |
description |
The inorganic-organic hybrid [VIV4O 10VV2O4] (C6H 14N2)•H2O polymeric framework was prepared under mild hydrothermal conditions from a mixture of DABCO and V 2O5 in deionized water with a 1:1:450 mole ratio, at neutral pH. The reaction was carried out at 180°C for 3 days under autogenous pressure yielding phase pure crystals product. The crystal structure was studied using both powder and single crystal X-ray crystallography, revealing the structure to be of the ({UuDd}:T*)α′ type in the SP+T class and Z-T subclass. The presence of the organic cation was confirmed by FT-IR spectrum and chemical composition analysis. The structure was thermally stable up to over 400°C, and showed ferromagnetic character at room temperature with the maximum molar susceptibility of 8.26 × 10 -3 emu/mol-1 at zero applied field. © 2006 Springer Science+Business Media, LLC. |
format |
Article |
author |
Settheeworrarit T. Pakawatchai C. Maensiri S. Limtrakul J. Rujiwatra A. |
spellingShingle |
Settheeworrarit T. Pakawatchai C. Maensiri S. Limtrakul J. Rujiwatra A. Crystal structure, thermal and magnetic behavior of inorganic-organic hybrid [VIV4O10 VV2O4] (C6H14N2) •H2O polymeric framework |
author_facet |
Settheeworrarit T. Pakawatchai C. Maensiri S. Limtrakul J. Rujiwatra A. |
author_sort |
Settheeworrarit T. |
title |
Crystal structure, thermal and magnetic behavior of inorganic-organic hybrid [VIV4O10 VV2O4] (C6H14N2) •H2O polymeric framework |
title_short |
Crystal structure, thermal and magnetic behavior of inorganic-organic hybrid [VIV4O10 VV2O4] (C6H14N2) •H2O polymeric framework |
title_full |
Crystal structure, thermal and magnetic behavior of inorganic-organic hybrid [VIV4O10 VV2O4] (C6H14N2) •H2O polymeric framework |
title_fullStr |
Crystal structure, thermal and magnetic behavior of inorganic-organic hybrid [VIV4O10 VV2O4] (C6H14N2) •H2O polymeric framework |
title_full_unstemmed |
Crystal structure, thermal and magnetic behavior of inorganic-organic hybrid [VIV4O10 VV2O4] (C6H14N2) •H2O polymeric framework |
title_sort |
crystal structure, thermal and magnetic behavior of inorganic-organic hybrid [viv4o10 vv2o4] (c6h14n2) •h2o polymeric framework |
publishDate |
2014 |
url |
http://www.scopus.com/inward/record.url?eid=2-s2.0-33750982096&partnerID=40&md5=6b70e1174abecdceae89cd3954d766ff http://cmuir.cmu.ac.th/handle/6653943832/5083 |
_version_ |
1681420358411878400 |