Fabrication and electrical properties of lead zirconate titanate-cement-epoxy composites
In this study, epoxy modified lead zirconate titanate-cement 0-3 and 1-3 composites were fabricated via two different techniques with epoxy added as the third phase. The 0-3 composites were fabricated by the normal paste mixing, while the 1-3 composites were fabricated using a dice-and-fill techniqu...
Saved in:
| Main Authors: | , , , , |
|---|---|
| Format: | Journal |
| Published: |
2018
|
| Subjects: | |
| Online Access: | https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=79955696594&origin=inward http://cmuir.cmu.ac.th/jspui/handle/6653943832/50939 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Institution: | Chiang Mai University |
| Summary: | In this study, epoxy modified lead zirconate titanate-cement 0-3 and 1-3 composites were fabricated via two different techniques with epoxy added as the third phase. The 0-3 composites were fabricated by the normal paste mixing, while the 1-3 composites were fabricated using a dice-and-fill technique. The dielectric and ferroelectric properties of the composites were examined. The results showed that dielectric constant (εr) at frequency of 1 kHz of 1-3 composites was higher and dielectric loss was lower than those of the 0-3 composite. The ferroelectric hysteresis loops agree with the results showing reduction area in lossy characteristic and the loops become more apparent in 1-3 composites. The use of epoxy results in a lower Pirvalue but a reduction in the lossy appearance of P-E loops is observed. |
|---|