Post-treatment by sodium silicate after zinc phosphating on cold-rolled steel
Post-treatment by sodium silicate after zinc phosphating on cold-rolled steel was studied. The steel substrates were firstly phosphated in a zinc-phosphating bath containing ZnO, NaF, H 3PO 4 and Ni(NO 3)...
Saved in:
| Main Authors: | , , |
|---|---|
| Format: | Journal |
| Published: |
2018
|
| Subjects: | |
| Online Access: | https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=84856583132&origin=inward http://cmuir.cmu.ac.th/jspui/handle/6653943832/51428 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Institution: | Chiang Mai University |
| Summary: | Post-treatment by sodium silicate after zinc phosphating on cold-rolled steel was studied. The steel substrates were firstly phosphated in a zinc-phosphating bath containing ZnO, NaF, H 3PO 4 and Ni(NO 3) 2 6H 2O under controlled conditions. Post-treatment by sodium silicate was consequently performed by varying the sodium silicate concentration and immersing time in the range of 33.3-100 wt% and 1-10 minutes, respectively. The coating layers before and after post-treatment were characterised by X-ray diffractometry and scanning electron microscopy-energy dispersive X-ray microanalysis. The phosphated layer was formed to be mainly hopeite and a minority of phosphophyllite, whereas the coating after post-treatment is mainly amorphous sodium silicate. The optimum post-treatment condition was using the 33.3 wt% sodium silicate solution at 5 minutes immersing time, by which an increase in corrosion resistance can be adequately obtained after post-treatment. |
|---|