Materials characterization of potassium sodium niobate based tellurite glass-ceramics
In this research, materials characterization of transparent glass-ceramics containing ferroelectric potassium sodium niobate (K0.5Na0.5)NbO3(KNN) crystals in a tellurite glass system were studied. The samples were prepared via an incorporation method. Glass-ceramics containing KNN crystals were succ...
Saved in:
| Main Authors: | , |
|---|---|
| Format: | Journal |
| Published: |
2018
|
| Subjects: | |
| Online Access: | https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=84878697959&origin=inward http://cmuir.cmu.ac.th/jspui/handle/6653943832/52560 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Institution: | Chiang Mai University |
| Summary: | In this research, materials characterization of transparent glass-ceramics containing ferroelectric potassium sodium niobate (K0.5Na0.5)NbO3(KNN) crystals in a tellurite glass system were studied. The samples were prepared via an incorporation method. Glass-ceramics containing KNN crystals were successfully fabricated by mixing KNN calcined powder with TeO2of about 70 and 80 mol% and melting at 800°C for 15 min in a platinum crucible. The prepared glasses were then subjected to heat treatment at 350-550°C. The optical properties of the samples were characterized by UV-Vis-NIR and ellipsometer. It was found that heat treatment temperature had significantly affected the optical properties. XRD patterns of the glass-ceramics revealed an amorphous-like structure with different degrees of crystallinity. SEM results confirmed the XRD data, where the degree of crystallinity increased with increasing heat treatment temperature. Copyright © Taylor & Francis Group, LLC. |
|---|