Temperature scaling of dynamic hysteresis in soft lead zirconate titanate bulk ceramic
The temperature scaling of the dynamic hysteresis was investigated in soft ferroelectric bulk ceramic. The power-law temperature scaling relations were obtained for hystersis area 〈A〉 and remnant polarization Pr, while the coercivity EC was found to scale linearly with temperature T. The three tempe...
محفوظ في:
| المؤلفون الرئيسيون: | , , , , , |
|---|---|
| التنسيق: | مقال |
| اللغة: | English |
| منشور في: |
2014
|
| الوصول للمادة أونلاين: | http://www.scopus.com/inward/record.url?eid=2-s2.0-33947327565&partnerID=40&md5=fe015f46d6f5c48d7de8510eedd9d0b3 http://cmuir.cmu.ac.th/handle/6653943832/5288 |
| الوسوم: |
إضافة وسم
لا توجد وسوم, كن أول من يضع وسما على هذه التسجيلة!
|
| المؤسسة: | Chiang Mai University |
| اللغة: | English |
| الملخص: | The temperature scaling of the dynamic hysteresis was investigated in soft ferroelectric bulk ceramic. The power-law temperature scaling relations were obtained for hystersis area 〈A〉 and remnant polarization Pr, while the coercivity EC was found to scale linearly with temperature T. The three temperature scaling relations were also field dependent. At fixed field amplitude E0, the scaling relations take the forms of 〈A〉 T-1.1024, Pr T-1.2322, and (EC0 - EC) T. Furthermore, the product of Pr and EC also provides the same scaling law on the T dependence in comparison with 〈A〉. © 2007 American Institute of Physics. |
|---|