Changes in ferroelectric properties of 0.7PMN-0.3PT ceramic with compressive stress
In this work, effects of compressive stress on the ferroelectric properties of 0.7PMN-0.3PT ceramics were investigated. The ceramics with the formula (0.7)Pb(Mg1/3Nb2/3O3-(0.3)PbTiO were prepared by a conventional mixed-oxide method. The ferroelectric properties under compressive stress were observe...
Saved in:
| Main Authors: | , , , , |
|---|---|
| Format: | Conference or Workshop Item |
| Language: | English |
| Published: |
2014
|
| Online Access: | http://www.scopus.com/inward/record.url?eid=2-s2.0-62949146491&partnerID=40&md5=d51765e02686a54566b3f938615a032a http://cmuir.cmu.ac.th/handle/6653943832/5378 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Institution: | Chiang Mai University |
| Language: | English |
| Summary: | In this work, effects of compressive stress on the ferroelectric properties of 0.7PMN-0.3PT ceramics were investigated. The ceramics with the formula (0.7)Pb(Mg1/3Nb2/3O3-(0.3)PbTiO were prepared by a conventional mixed-oxide method. The ferroelectric properties under compressive stress were observed at stress up to 80 MPa using a compressometer in conjunction with a modified Sawyer-Tower circuit. The results showed that applied stress had a significant influence on the ferroelectric properties of 0.7PMN-0.3PT ceramics. Ferroelectric characteristics, i.e. the area of the ferroelectric hysteresis (P-E) loop, the saturation polarization (P sat), the remanent polarization (Pr) and loop squareness (Rsq), decreased with increasing compressive stress, while the coercive field (Ec) remained relatively constant. Stress-induced domain wall motion suppression and non-180°C ferroelectric domain switching processes are responsible for the changes observed. © 2008 Trans Tech Publications, Switzerland. |
|---|