Dielectric and piezoelectric properties of zirconium-doped bismuth sodium titanate ceramics
Zirconium-doped bismuth sodium titanate ceramics were prepared using the conventional processing method. X-ray diffraction analysis indicated the materials were single phase with a systematic shift due to increased unit cell size. The measured densities and grain size of the ceramic samples were fou...
Saved in:
| Main Authors: | , |
|---|---|
| 格式: | Conference or Workshop Item |
| 語言: | English |
| 出版: |
2014
|
| 在線閱讀: | http://www.scopus.com/inward/record.url?eid=2-s2.0-62949214245&partnerID=40&md5=b240da2ddac4a40bac91ad7cd139a622 http://cmuir.cmu.ac.th/handle/6653943832/5436 |
| 標簽: |
添加標簽
沒有標簽, 成為第一個標記此記錄!
|
| 總結: | Zirconium-doped bismuth sodium titanate ceramics were prepared using the conventional processing method. X-ray diffraction analysis indicated the materials were single phase with a systematic shift due to increased unit cell size. The measured densities and grain size of the ceramic samples were found to range from 5.79-6.03 g/cm3 and 0.5-1.6 μm, respectively. The dielectric constant as a function of temperature became broader as Zr content increased. The piezoelectric constant was found to decrease with increasing Zr. Within the range of the solid solutions investigated, the materials seem to be promising for high temperature applications where stable dielectric constant is required. © 2008 Trans Tech Publications, Switzerland. |
|---|