Enhanced dielectric and ferroelectric properties of Pb(Mg<inf>1/3</inf>Nb<inf>2/3</inf>)<inf>0.65</inf>Ti<inf>0.35</inf>O<inf>3</inf>ceramics by ZnO modification
© 2014 The American Ceramic Society. Phase formation, microstructures, dielectric, and ferroelectric properties of ZnO-modified Pb(Mg1/3Nb2/3)0.65Ti0.35O3(PMNT/xZnO, where x = 0, 0.4, 2.0, 4.0, and 11.0 mol%) ceramics were studied. A coexistence of rhombohedral and tetragonal ferroelectric phases wa...
Saved in:
| Main Authors: | , , , |
|---|---|
| Format: | Journal |
| Published: |
2018
|
| Subjects: | |
| Online Access: | https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=85027920759&origin=inward http://cmuir.cmu.ac.th/jspui/handle/6653943832/54440 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Institution: | Chiang Mai University |
| Summary: | © 2014 The American Ceramic Society. Phase formation, microstructures, dielectric, and ferroelectric properties of ZnO-modified Pb(Mg1/3Nb2/3)0.65Ti0.35O3(PMNT/xZnO, where x = 0, 0.4, 2.0, 4.0, and 11.0 mol%) ceramics were studied. A coexistence of rhombohedral and tetragonal ferroelectric phases was observed at room temperature in all samples. The ceramics with the relative densities of 93%-95% were prepared. The modification by ZnO led to an increase in grain sizes of PMNT ceramics. The maximum dielectric constant of the pure PMNT ceramic was increased with x = 0.4-4.0 mol% ZnO doping, with the highest value being observed in the 2.0 mol% sample. Both the temperature at which the transition between rhombohedral and tetragonal ferroelectric phases took place (TR-T) and the Curie temperature of the ceramics tended to increase with increasing x. The ferroelectric properties were enhanced with increased remanent polarization and P(E) loop squareness in the compositions with x = 0.4-4.0 mol%. However, the ferroelectric properties were attenuated with x = 11.0 mol%. |
|---|