Microwave synthesis of barium iron niobate and dielectric properties
A microwave synthesis was applied to prepare barium iron niobate (BFN) powders for the first time. Pure perovskite phase of BFN with a cubic symmetry was obtained when precursors were calcined at 850 °C for 14 h. Average particle size of pure BFN powder was estimated to be in submicron range. The ex...
Saved in:
Main Authors: | Charoenthai N., Traiphol R., Rujijanagul G. |
---|---|
Format: | Article |
Language: | English |
Published: |
2014
|
Online Access: | http://www.scopus.com/inward/record.url?eid=2-s2.0-51349125589&partnerID=40&md5=28324362b7b0b0690411c62e84fc13bf http://cmuir.cmu.ac.th/handle/6653943832/5447 |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Institution: | Chiang Mai University |
Language: | English |
Similar Items
-
Microwave synthesis of barium iron niobate and dielectric properties
by: Nipaphat Charoenthai, et al.
Published: (2018) -
Preparation and dielectric properties of barium iron niobate by molten-salt synthesis
by: Tawichai N., et al.
Published: (2014) -
Preparation and dielectric properties of barium iron niobate by molten-salt synthesis
by: Tawichai,N., et al.
Published: (2015) -
Dielectric properties of Ga2O3-doped barium iron niobate ceramics
by: Sanjoom,K., et al.
Published: (2015) -
Phase evolution and dielectric properties of barium zirconate titanate - Barium iron niobate ceramics
by: Intatha U., et al.
Published: (2014)