Raman scattering and electrical conductivity of nitrogen implanted MoO3 whiskers
Whiskers of MoO3 have been grown by a thermal transport process. A set of samples was then implanted with nitrogen ions at a dose of 5 × 1016 ion/cm2. The implanted whiskers changed from transparent to semi-transparent. Raman spectroscopy of the whiskers was observed and compared with those of unimp...
Saved in:
Main Authors: | , , , |
---|---|
Format: | Article |
Language: | English |
Published: |
2014
|
Online Access: | http://www.scopus.com/inward/record.url?eid=2-s2.0-42649105811&partnerID=40&md5=f41d682fc91095c817c0c2efeab6b84b http://cmuir.cmu.ac.th/handle/6653943832/5558 |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Institution: | Chiang Mai University |
Language: | English |
id |
th-cmuir.6653943832-5558 |
---|---|
record_format |
dspace |
spelling |
th-cmuir.6653943832-55582014-08-30T02:56:40Z Raman scattering and electrical conductivity of nitrogen implanted MoO3 whiskers Phadungdhitidhada S. Mangkorntong P. Choopun S. Mangkorntong N. Whiskers of MoO3 have been grown by a thermal transport process. A set of samples was then implanted with nitrogen ions at a dose of 5 × 1016 ion/cm2. The implanted whiskers changed from transparent to semi-transparent. Raman spectroscopy of the whiskers was observed and compared with those of unimplanted whiskers. The results revealed that the Raman intensity of the implanted whiskers was decreased about 10 times with respect to that of unimplanted whiskers. Only the case of the wave propagation parallel to the a-axis, a lower suppression ratio of the B3g modes was observed. No extra mode due to the nitrogen implantation was observed. This indicates that implantation could only induce defects and oxygen vacancies but not the structural transformation. From electrical conductivity and Hall measurement, it was found that the whiskers exhibited an n-type semiconductor and its conductivity drastically increased due to the defects and oxygen vacancies. © 2007 Elsevier Ltd and Techna Group S.r.l. 2014-08-30T02:56:40Z 2014-08-30T02:56:40Z 2008 Article 02728842 10.1016/j.ceramint.2007.09.093 CINND http://www.scopus.com/inward/record.url?eid=2-s2.0-42649105811&partnerID=40&md5=f41d682fc91095c817c0c2efeab6b84b http://cmuir.cmu.ac.th/handle/6653943832/5558 English |
institution |
Chiang Mai University |
building |
Chiang Mai University Library |
country |
Thailand |
collection |
CMU Intellectual Repository |
language |
English |
description |
Whiskers of MoO3 have been grown by a thermal transport process. A set of samples was then implanted with nitrogen ions at a dose of 5 × 1016 ion/cm2. The implanted whiskers changed from transparent to semi-transparent. Raman spectroscopy of the whiskers was observed and compared with those of unimplanted whiskers. The results revealed that the Raman intensity of the implanted whiskers was decreased about 10 times with respect to that of unimplanted whiskers. Only the case of the wave propagation parallel to the a-axis, a lower suppression ratio of the B3g modes was observed. No extra mode due to the nitrogen implantation was observed. This indicates that implantation could only induce defects and oxygen vacancies but not the structural transformation. From electrical conductivity and Hall measurement, it was found that the whiskers exhibited an n-type semiconductor and its conductivity drastically increased due to the defects and oxygen vacancies. © 2007 Elsevier Ltd and Techna Group S.r.l. |
format |
Article |
author |
Phadungdhitidhada S. Mangkorntong P. Choopun S. Mangkorntong N. |
spellingShingle |
Phadungdhitidhada S. Mangkorntong P. Choopun S. Mangkorntong N. Raman scattering and electrical conductivity of nitrogen implanted MoO3 whiskers |
author_facet |
Phadungdhitidhada S. Mangkorntong P. Choopun S. Mangkorntong N. |
author_sort |
Phadungdhitidhada S. |
title |
Raman scattering and electrical conductivity of nitrogen implanted MoO3 whiskers |
title_short |
Raman scattering and electrical conductivity of nitrogen implanted MoO3 whiskers |
title_full |
Raman scattering and electrical conductivity of nitrogen implanted MoO3 whiskers |
title_fullStr |
Raman scattering and electrical conductivity of nitrogen implanted MoO3 whiskers |
title_full_unstemmed |
Raman scattering and electrical conductivity of nitrogen implanted MoO3 whiskers |
title_sort |
raman scattering and electrical conductivity of nitrogen implanted moo3 whiskers |
publishDate |
2014 |
url |
http://www.scopus.com/inward/record.url?eid=2-s2.0-42649105811&partnerID=40&md5=f41d682fc91095c817c0c2efeab6b84b http://cmuir.cmu.ac.th/handle/6653943832/5558 |
_version_ |
1681420448329367552 |