Electrical properties of ternary system Bi<inf>0.5</inf>(Na<inf>0.80</inf>K<inf>0.20</inf>)<inf>0.5</inf>TiO<inf>3</inf>-0.005LiNbO<inf>3</inf>-BaTiO<inf>3</inf>lead-free piezoelectric ceramics
© 2016 Taylor & Francis Group, LLC. Ternary system of lead-free piezoelectric ceramics with the formula of (1-x-y)Bi0.5(Na0.80K0.20)0.5TiO3-xLiNbO3-yBaTiO3or (1-x-y)BNKT-xLN-yBT (x = 0.005 and y = 0, 0.01, 0.02, 0.03, 0.04, 0.05, 0.06 and 0.07 mol fraction) were sintered at the temperature of...
Saved in:
| Main Authors: | , , , |
|---|---|
| Format: | Journal |
| Published: |
2018
|
| Subjects: | |
| Online Access: | https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=84982300284&origin=inward http://cmuir.cmu.ac.th/jspui/handle/6653943832/55721 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Institution: | Chiang Mai University |
| Summary: | © 2016 Taylor & Francis Group, LLC. Ternary system of lead-free piezoelectric ceramics with the formula of (1-x-y)Bi0.5(Na0.80K0.20)0.5TiO3-xLiNbO3-yBaTiO3or (1-x-y)BNKT-xLN-yBT (x = 0.005 and y = 0, 0.01, 0.02, 0.03, 0.04, 0.05, 0.06 and 0.07 mol fraction) were sintered at the temperature of 1125°C for 2 h. All samples have the density ranging of 5.59 - 5.73 g/cm3. X-ray diffraction pattern exhibited a single perovskite structure without any secondary phase. Scanning electron micrographs indicated a cubic-like grain shape occurred for all compositions with side length of 0.49 - 0.77 μm. At a composition BNKT-0.005LN-0.04BT showed the highest piezoelectric coefficient (d33= 198 pC/N) with good dielectric (ϵr= 1775, tanδ = 0.0534) and ferroelectric properties (Pr= 17.36 μC/cm2, Rsq= 1.67). |
|---|