The effect of alumina (Al<inf>2</inf>O<inf>3</inf>) on the characteristics of sintered mullite-cordierite ceramics synthesized with kaolin from naratiwas of Thailand
© 2016 Trans Tech Publications, Switzerland. Mullite-cordierite ceramics was prepared by the three composition of talc, kaolin (kaolin from Naratiwas in Thailand) (NT) and alumina. The different amounts of alumina (5, 10, 15 and 20 wt%) were added to produce various mullite-cordierite alumina mixtur...
محفوظ في:
| المؤلفون الرئيسيون: | , |
|---|---|
| التنسيق: | Book Series |
| منشور في: |
2018
|
| الموضوعات: | |
| الوصول للمادة أونلاين: | https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=84970003173&origin=inward http://cmuir.cmu.ac.th/jspui/handle/6653943832/55816 |
| الوسوم: |
إضافة وسم
لا توجد وسوم, كن أول من يضع وسما على هذه التسجيلة!
|
| المؤسسة: | Chiang Mai University |
| الملخص: | © 2016 Trans Tech Publications, Switzerland. Mullite-cordierite ceramics was prepared by the three composition of talc, kaolin (kaolin from Naratiwas in Thailand) (NT) and alumina. The different amounts of alumina (5, 10, 15 and 20 wt%) were added to produce various mullite-cordierite alumina mixtures which are denoted as NA, NB, NC and ND, respectively. The mixtures were pressed into rectangular shapes by hydraulic press with the pressure of 150 kg/cm2then sintered at temperature of 1300 °C and 1350 °C for 2 hours. The morphology of the synthesized mullite-cordierite samples were characterized by x-ray diffraction spectroscopy (XRD), and physical-mechanical properties were investigated. Mullitecordierite was successfully synthesized. The XRD result was represented phases of mullite and cordierite. The NA samples sintered at temperature of 1300 °C indicated the best physicalmechanical properties including bulk density (2.23 g/cm3), flexural strength (44.4 MPa) and thermal expansion coefficients (5.00x10-6). The other NA samples sintered at temperature of 1350 °C exhibited the bulk density, flexural strength and thermal expansion coefficients are 2.21 g/cm3, 47.8 MPa and 4.99 x10-6, respectively. The thermal expansion coefficient of the NT sintered samples have been plotted the length change relative to measuring temperature ranging of 30-1200 °C. The suitable condition of the synthesized mullite-cordierite ceramics is finally obtained the NA samples with 5 percent weight of alumina composition sintered at the temperature of 1350 °C. |
|---|