Stress dependent ferroelectric properties of PZT and 0.9PZT - 0.1BLT ceramics
P-E hysteresis loops of PZT and 0.9PZT - 0.1BLT ceramics were determined using a modified Sawyer-Tower circuit. Ferroelectric properties investigation of the PZT and 0.9PZT - 0.1BLT ceramics under stress levels in the range of 0-175 MPa was also carried out. The result showed that with increasing st...
محفوظ في:
| المؤلفون الرئيسيون: | , , , , |
|---|---|
| التنسيق: | Conference or Workshop Item |
| اللغة: | English |
| منشور في: |
2014
|
| الوصول للمادة أونلاين: | http://www.scopus.com/inward/record.url?eid=2-s2.0-77949280940&partnerID=40&md5=82df90ef7e206a2e139bae61da1330be http://cmuir.cmu.ac.th/handle/6653943832/5717 |
| الوسوم: |
إضافة وسم
لا توجد وسوم, كن أول من يضع وسما على هذه التسجيلة!
|
| الملخص: | P-E hysteresis loops of PZT and 0.9PZT - 0.1BLT ceramics were determined using a modified Sawyer-Tower circuit. Ferroelectric properties investigation of the PZT and 0.9PZT - 0.1BLT ceramics under stress levels in the range of 0-175 MPa was also carried out. The result showed that with increasing stress level, a reduction of remanent polarization was clearly observed. The result was interpreted in terms of non-180° ferroelectric domain switching processes and the decrease in switchable part of domains induced by stress applied to these materials. Copyright © Taylor & Francis Group, LLC. |
|---|