Influence of sintering temperature on dielectric and piezoelectric properties of B2O3 doped lead-free Ba(Ti 0.9Sn0.1)O3 ceramics
Lead-free ceramics of Ba(Ti0.9Sn0.1)O3 doped with 0.5 wt% B2O3 were prepared by a conventional solid state sintering method. Dielectric and piezoelectric properties of the ceramics were investigated as a function of sintering temperature. Although density of the ceramics was observed to decrease wit...
محفوظ في:
| المؤلفون الرئيسيون: | , |
|---|---|
| التنسيق: | Conference or Workshop Item |
| اللغة: | English |
| منشور في: |
2014
|
| الوصول للمادة أونلاين: | http://www.scopus.com/inward/record.url?eid=2-s2.0-77949346944&partnerID=40&md5=7212fe4d124dd3be8ae796579a260d5e http://cmuir.cmu.ac.th/handle/6653943832/5725 |
| الوسوم: |
إضافة وسم
لا توجد وسوم, كن أول من يضع وسما على هذه التسجيلة!
|
| الملخص: | Lead-free ceramics of Ba(Ti0.9Sn0.1)O3 doped with 0.5 wt% B2O3 were prepared by a conventional solid state sintering method. Dielectric and piezoelectric properties of the ceramics were investigated as a function of sintering temperature. Although density of the ceramics was observed to decrease with increasing the sintering temperature, the sample sintered at 1350°C showed maximum dielectric constant of 9900 at the phase transition temperature ∼36°C. Higher relative tunability of 83% was also observed at the same condition. However, the ceramics showed a lower piezoelectric coefficient (d33) at a higher sintering temperature. Copyright © Taylor & Francis Group, LLC. |
|---|