Sol-gel derived PZT and PZTN ceramics: A role of sintering temperature
PZT and Nb-doped PZT (PZTN) ceramics were fabricated from triol sol-gel derived powders. The pellets were sintered at temperatures in the range of 1050-1200°C for 2 h. Coexistence of tetragonal and rhombohedral phases was clearly observed in PZT ceramics sintered at ≤1150°C, while PZTN ceramics show...