Effects of sintering conditions on phase formation and dielectric properties of 0.8Pb (Zr1/2Ti1/2) O3 -0.2Pb(Co1/3Nb2/3)O3 ceramics

The influences of sintering conditions on dielectric properties of the 0.8Pb(Zr1/2Ti1/2)O3 -0.2Pb(Co1/3Nb2/3)O3 ceramics have been investigated with sintering temperatures of 1175, 1200°, 1225, and 1250°C and dwell times for 2, 6, and 10 hours. The crystal structure of dense specimens showed coexist...

Full description

Saved in:
Bibliographic Details
Main Authors: Prasatkhetragarn A., Ketsuwan P., Unruan M., Ngamjarurojana A., Laosiritaworn Y., Ananta S., Yimnirun R., Cann D.P.
Format: Conference or Workshop Item
Language:English
Published: 2014
Online Access:http://www.scopus.com/inward/record.url?eid=2-s2.0-77949300571&partnerID=40&md5=c016c4c2217504de74c04d4e171f6edd
http://cmuir.cmu.ac.th/handle/6653943832/5754
Tags: Add Tag
No Tags, Be the first to tag this record!
Institution: Chiang Mai University
Language: English
Description
Summary:The influences of sintering conditions on dielectric properties of the 0.8Pb(Zr1/2Ti1/2)O3 -0.2Pb(Co1/3Nb2/3)O3 ceramics have been investigated with sintering temperatures of 1175, 1200°, 1225, and 1250°C and dwell times for 2, 6, and 10 hours. The crystal structure of dense specimens showed coexistence between tetragonal, rhombohedral and pseudo cubic phases in all sintering temperatures, while tetragonal-rich phase appeared with increasing dwell times. A maximum dielectric constant was observed at sintering condition of 1200°C for 2 hours, while the transition temperature slightly increased with increasing dwell time. All ceramics also showed diffused phase transition behaviors with a minimum diffusivity at sintering condition of 1200°C for 2 hours. Copyright © Taylor & Francis Group, LLC.