Effect of basicity on the morphologies of ZnO produced using a sonochemical method
Wurtzite ZnO was produced by the sonochemical reactions of 0.005 mol Zn(NO3)2 and different moles of NaOH in de-ionized water. The phase was characterized using X-ray diffraction (XRD) and selected area electron diffraction (SAED). A Raman peak was clearly detected at 435 cm-1. The SAED patterns wer...
محفوظ في:
| المؤلفون الرئيسيون: | , , |
|---|---|
| التنسيق: | مقال |
| اللغة: | English |
| منشور في: |
2014
|
| الوصول للمادة أونلاين: | http://www.scopus.com/inward/record.url?eid=2-s2.0-67349284700&partnerID=40&md5=974ede01ee302c6456e3d21ee883df35 http://cmuir.cmu.ac.th/handle/6653943832/5893 |
| الوسوم: |
إضافة وسم
لا توجد وسوم, كن أول من يضع وسما على هذه التسجيلة!
|
| المؤسسة: | Chiang Mai University |
| اللغة: | English |
| الملخص: | Wurtzite ZnO was produced by the sonochemical reactions of 0.005 mol Zn(NO3)2 and different moles of NaOH in de-ionized water. The phase was characterized using X-ray diffraction (XRD) and selected area electron diffraction (SAED). A Raman peak was clearly detected at 435 cm-1. The SAED patterns were in accordance with those of the simulation. Scanning and transmission electron microscopies (SEM and TEM) revealed the presence of 72 ± 17 nm nano-particles, and nano-plates and spear-shaped particles in flower-like clusters, influenced by basicity conditions. By using high-resolution TEM (HRTEM), a spear was observed growing in the [0 0 1] direction normal to its (0 0 2) plane. © 2009 Elsevier B.V. All rights reserved. |
|---|