Ferroelectric properties of Pb(Zr1/2Ti1/2)O3-Pb(Zn1/3Nb2/3)O3 ceramics under compressive stress

• Main Authors: Yimnirun R., Triamnak N., Unruan M., Ngamjarurojana A., Laosiritaworn Y., Ananta S.
• Format: Article
• Language: English
• Published: 2014
• Online Access: http://www.scopus.com/inward/record.url?eid=2-s2.0-51249107339&partnerID=40&md5=cbc5609ca23d0b2516a7e792d6041957; http://cmuir.cmu.ac.th/handle/6653943832/5956
• Institution: Chiang Mai University

Effects of compressive stress on the ferroelectric properties of ceramics in PZT-PZN system were investigated. The ceramics with a formula (1-x)Pb(Zr1/2Ti1/2)O3-xPb(Zn1/3Nb2/3)O3 or (1-x)PZT-(x)PZN (x = 0.1-0.5) were prepared by a conventional mixed-oxide method. The ferroelectric properties under the compressive stress of the PZT-PZN ceramics were observed at the stress levels up to 170 MPa using a compressometer in conjunction with a modified Sawyer-Tower circuit. It was found that with increasing compressive stress the area of the ferroelectric hysteresis (P-E) loops, the saturation polarization (Psat), the remnant polarization (Pr), and the coercive field (Ec) decreased. These results were interpreted through the non-180° ferroelastic domain switching processes. © 2008 Elsevier B.V. All rights reserved.