Fabrication and characterization of (1-x)BiFeO<inf>3</inf>-xBaTiO<inf>3</inf> ceramics prepared by a solid state reaction method

• Main Authors: S. Chandarak, M. Unruan, T. Sareein, A. Ngamjarurojana, S. Maensiri, P. Laoratanakul, S. Ananta, R. Yimnirun
• Format: Journal
• Published: 2018
• Subjects: Engineering; Materials Science; Physics and Astronomy
• Online Access: https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=70349985118&origin=inward; http://cmuir.cmu.ac.th/jspui/handle/6653943832/59567
• Institution: Chiang Mai University

In this study, BiFeO3-BaTiO3 ceramics have been fabricated by a solid-state reaction method. The effects of BaTiO3 content in the (1-x)BiFeO3-xBaTiO3 (x = 0.1, 0.2, 0.25, 0.3, 0.4, 0.5) system on crystal structure and magnetic, dielectric, and ferroelectric properties were investigated. Perovskite BiFeO3 was stabilized through the formation of a solid solution with BaTiO3. Rhombohedrally distorted structure (1-x)BiFeO3-xBaTiO3 ceramics showed strong ferromagnetism at x = 0.5. Dielectric and ferroelectric properties of the BiFeO3-BaTiO3 system also changed significantly upon addition of BaTiO3. It was found that the maximum dielectric and ferroelectric properties were exhibited in the (1-x)BiFeO3-xBaTiO3 system at x = 0.25. This suggested the morphotropic phase boundary (MPB) with the coexistence of both rhombohedral and cubic phases of the (1-x)BiFeO3-xBaTiO3 system at x = 0.25. © 2009 Journal of Magnetics.