Stress dependent ferroelectric properties of PZT and 0.9PZT - 0.1BLT ceramics
P-E hysteresis loops of PZT and 0.9PZT - 0.1BLT ceramics were determined using a modified Sawyer-Tower circuit. Ferroelectric properties investigation of the PZT and 0.9PZT - 0.1BLT ceramics under stress levels in the range of 0-175 MPa was also carried out. The result showed that with increasing st...
Saved in:
| Main Authors: | , , , , |
|---|---|
| Format: | Journal |
| Published: |
2018
|
| Subjects: | |
| Online Access: | https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=77949280940&origin=inward http://cmuir.cmu.ac.th/jspui/handle/6653943832/59656 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Institution: | Chiang Mai University |
| Summary: | P-E hysteresis loops of PZT and 0.9PZT - 0.1BLT ceramics were determined using a modified Sawyer-Tower circuit. Ferroelectric properties investigation of the PZT and 0.9PZT - 0.1BLT ceramics under stress levels in the range of 0-175 MPa was also carried out. The result showed that with increasing stress level, a reduction of remanent polarization was clearly observed. The result was interpreted in terms of non-180° ferroelectric domain switching processes and the decrease in switchable part of domains induced by stress applied to these materials. Copyright © Taylor & Francis Group, LLC. |
|---|