Electrical properties of Nb-DOPED Pb(Zr<inf>0.52</inf>Ti<inf>0.48</inf>)O<inf>3</inf>ceramics
The Pb(Zr0.52Ti0.48)O3ceramics with 0.75, 1.0, 1.25 and 1.50%wt of Nb2O5addition were prepared by a conventional mixed oxide technique. It was found that the average grain size of the ceramics decreased from 6 to 1 μm with increasing doping concentration to 1.5%wt. The room temperature dielectric co...
محفوظ في:
| المؤلفون الرئيسيون: | , , , |
|---|---|
| التنسيق: | دورية |
| منشور في: |
2018
|
| الموضوعات: | |
| الوصول للمادة أونلاين: | https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=66249116335&origin=inward http://cmuir.cmu.ac.th/jspui/handle/6653943832/59955 |
| الوسوم: |
إضافة وسم
لا توجد وسوم, كن أول من يضع وسما على هذه التسجيلة!
|
| المؤسسة: | Chiang Mai University |
| الملخص: | The Pb(Zr0.52Ti0.48)O3ceramics with 0.75, 1.0, 1.25 and 1.50%wt of Nb2O5addition were prepared by a conventional mixed oxide technique. It was found that the average grain size of the ceramics decreased from 6 to 1 μm with increasing doping concentration to 1.5%wt. The room temperature dielectric constant and d33reached maximum values of 1050 and 285 pC/N, respectively, at 1%wt Nb-doping. The electrical coercivity (Ec) of Nb-doped PZT decreased, while the polarization values increased, with increasing doping concentration. Most importantly, this study shows that Nb2O5-doped PZT ceramics exhibits soft piezoelectric and enhanced ferroelectric behaviors, and the optimum properties can be obtained using suitable doping concentration. © 2009 World Scientific Publishing Company. |
|---|