Photocatalytic property of colloidal TiO2 nanoparticles prepared by sparking process
Titanium oxide nanoparticles (NPs) were successfully prepared by sparking off two titanium tips into water for 1-5 h. The nanoparticle-dispersed water was obtained for further characterization. The transmission electron microscopy result shows that the particle size is in the range of 1-5 nm. The el...
Saved in:
Main Authors: | , , |
---|---|
Format: | Journal |
Published: |
2018
|
Subjects: | |
Online Access: | https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=44149111328&origin=inward http://cmuir.cmu.ac.th/jspui/handle/6653943832/60508 |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Institution: | Chiang Mai University |
id |
th-cmuir.6653943832-60508 |
---|---|
record_format |
dspace |
spelling |
th-cmuir.6653943832-605082018-09-10T03:48:23Z Photocatalytic property of colloidal TiO2 nanoparticles prepared by sparking process W. Thongsuwan T. Kumpika P. Singjai Materials Science Physics and Astronomy Titanium oxide nanoparticles (NPs) were successfully prepared by sparking off two titanium tips into water for 1-5 h. The nanoparticle-dispersed water was obtained for further characterization. The transmission electron microscopy result shows that the particle size is in the range of 1-5 nm. The electron diffraction patterns and Raman spectra reveal that the as-prepared and the annealed samples at 250 °C are the anatase phase. However, the anatase-rutile phase transformation was observed from the samples at annealing temperature as low as 500 °C. The result of methylene blue-decoloration testing under sunbath suggests that the NPs have good photocatalytic property. © 2007 Elsevier B.V. All rights reserved. 2018-09-10T03:44:07Z 2018-09-10T03:44:07Z 2008-08-01 Journal 15671739 2-s2.0-44149111328 10.1016/j.cap.2007.10.004 https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=44149111328&origin=inward http://cmuir.cmu.ac.th/jspui/handle/6653943832/60508 |
institution |
Chiang Mai University |
building |
Chiang Mai University Library |
country |
Thailand |
collection |
CMU Intellectual Repository |
topic |
Materials Science Physics and Astronomy |
spellingShingle |
Materials Science Physics and Astronomy W. Thongsuwan T. Kumpika P. Singjai Photocatalytic property of colloidal TiO2 nanoparticles prepared by sparking process |
description |
Titanium oxide nanoparticles (NPs) were successfully prepared by sparking off two titanium tips into water for 1-5 h. The nanoparticle-dispersed water was obtained for further characterization. The transmission electron microscopy result shows that the particle size is in the range of 1-5 nm. The electron diffraction patterns and Raman spectra reveal that the as-prepared and the annealed samples at 250 °C are the anatase phase. However, the anatase-rutile phase transformation was observed from the samples at annealing temperature as low as 500 °C. The result of methylene blue-decoloration testing under sunbath suggests that the NPs have good photocatalytic property. © 2007 Elsevier B.V. All rights reserved. |
format |
Journal |
author |
W. Thongsuwan T. Kumpika P. Singjai |
author_facet |
W. Thongsuwan T. Kumpika P. Singjai |
author_sort |
W. Thongsuwan |
title |
Photocatalytic property of colloidal TiO2 nanoparticles prepared by sparking process |
title_short |
Photocatalytic property of colloidal TiO2 nanoparticles prepared by sparking process |
title_full |
Photocatalytic property of colloidal TiO2 nanoparticles prepared by sparking process |
title_fullStr |
Photocatalytic property of colloidal TiO2 nanoparticles prepared by sparking process |
title_full_unstemmed |
Photocatalytic property of colloidal TiO2 nanoparticles prepared by sparking process |
title_sort |
photocatalytic property of colloidal tio2 nanoparticles prepared by sparking process |
publishDate |
2018 |
url |
https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=44149111328&origin=inward http://cmuir.cmu.ac.th/jspui/handle/6653943832/60508 |
_version_ |
1681425448656961536 |