H(2) Sensing Response of Flame-Spray-Made Ru/SnO(2) Thick Films Fabricated from Spin-Coated Nanoparticles
High specific surface area (SSA(BET): 141.6 m(2)/g) SnO(2) nanoparticles doped with 0.2-3 wt% Ru were successfully produced in a single step by flame spray pyrolysis (FSP). The phase and crystallite size were analyzed by XRD. The specific surface area (SSA(BET)) of the nanoparticles was measured by...
Saved in:
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
2014
|
| Online Access: | http://www.ncbi.nlm.nih.gov/pubmed/3502482 http://cmuir.cmu.ac.th/handle/6653943832/6071 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Institution: | Chiang Mai University |
| Language: | English |
| Summary: | High specific surface area (SSA(BET): 141.6 m(2)/g) SnO(2) nanoparticles doped with 0.2-3 wt% Ru were successfully produced in a single step by flame spray pyrolysis (FSP). The phase and crystallite size were analyzed by XRD. The specific surface area (SSA(BET)) of the nanoparticles was measured by nitrogen adsorption (BET analysis). As the Ru concentration increased, the SSA(BET) was found to linearly decrease, while the average BET-equivalent particle diameter (d(BET)) increased. FSP yielded small Ru particles attached to the surface of the supporting SnO(2) nanoparticles, indicating a high SSA(BET). The morphology and accurate size of the primary particles were further investigated by TEM. The crystallite sizes of the spherical, hexagonal, and rectangular SnO(2) particles were in the range of 3-10 nm. SnO(2) nanorods were found to range from 3-5 nm in width and 5-20 nm in length. Sensing films were prepared by the spin coating technique. The gas sensing of H(2) (500-10,000 ppm) was studied at the operating temperatures ranging from 200-350 °C in presence of dry air. After the sensing tests, the morphology and the cross-section of sensing film were analyzed by SEM and EDS analyses. The 0.2%Ru-dispersed on SnO(2) sensing film showed the highest sensitivity and a very fast response time (6 s) compared to a pure SnO(2) sensing film, with a highest H(2) concentration of 1 vol% at 350 °C and a low H(2) detection limit of 500 ppm at 200 °C. |
|---|