Characterization and properties of Sb-doped BaTi O3 powders
Improved single-phase nanocrystalline BaTi O3 powders may be prepared at 700 °C by the sol-gel acetate process to which 1-3 wt % Sb is added as dopant. Following calcination at 1200 °C, the resulting average particle size as determined by scanning electron microscopy analysis is in the range of 50-1...
Saved in:
| Main Authors: | , |
|---|---|
| 格式: | 雜誌 |
| 出版: |
2018
|
| 主題: | |
| 在線閱讀: | https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=33847169450&origin=inward http://cmuir.cmu.ac.th/jspui/handle/6653943832/61398 |
| 標簽: |
添加標簽
沒有標簽, 成為第一個標記此記錄!
|
| 機構: | Chiang Mai University |
| 總結: | Improved single-phase nanocrystalline BaTi O3 powders may be prepared at 700 °C by the sol-gel acetate process to which 1-3 wt % Sb is added as dopant. Following calcination at 1200 °C, the resulting average particle size as determined by scanning electron microscopy analysis is in the range of 50-150 nm. The dielectric results show that fired samples containing 1 wt % Sb have the highest relative permittivity, with εr ≈4500 and TC =52 °C, whereas undoped samples have εr ≈3300 and TC =120 °C. © 2007 American Institute of Physics. |
|---|