Effect of temperature on the dielectric properties of 0-3 PZT-cement composites

In this work, 0-3 lead zirconate titanate (PZT) was mixed with normal Portland cement to produce 0-3 connectivity composites. The effect of temperature on the dielectric properties such as the dielectric constant and dielectric loss was determined. It was found that with increasing PZT content the T...

Full description

Saved in:
Bibliographic Details
Main Authors: Chaipanich A., Rianyoi R., Potong R., Jaitanong N.
Format: Article
Language:English
Published: 2014
Online Access:http://www.scopus.com/inward/record.url?eid=2-s2.0-79955419212&partnerID=40&md5=c7f83e655463f586d171c21427b7cea7
http://cmuir.cmu.ac.th/handle/6653943832/6153
Tags: Add Tag
No Tags, Be the first to tag this record!
Institution: Chiang Mai University
Language: English
Description
Summary:In this work, 0-3 lead zirconate titanate (PZT) was mixed with normal Portland cement to produce 0-3 connectivity composites. The effect of temperature on the dielectric properties such as the dielectric constant and dielectric loss was determined. It was found that with increasing PZT content the Tc increases where the optimum dielectric constant was observed and that at the temperature up to 100°C there is a significant change in the dielectric properties in PZT-cement composites. This is due to the loss of water molecules at up to 100°C. At above 100°C, the dielectric properties of the composites were found to have a similar behavior to that of PZT ceramic with Tc being ≈420°C.