Effects of alumina surrounding in sintering process on ZnO-Bi<inf>2</inf>O<inf>3</inf>varistors doped with CoO
Nonlinear current-voltage properties of zinc oxide-bismuth oxide varistors doped with cobalt oxide were investigated. The composition of ZnO doped with 0.5 mol% Bi2O3and 0.75 mol%CoO was prepared and sintered in two different surroundings, zinc oxide-bismuth oxide-cobalt oxide powder and alumina pow...
محفوظ في:
| المؤلفون الرئيسيون: | , , |
|---|---|
| التنسيق: | دورية |
| منشور في: |
2018
|
| الموضوعات: | |
| الوصول للمادة أونلاين: | https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=9644272421&origin=inward http://cmuir.cmu.ac.th/jspui/handle/6653943832/62217 |
| الوسوم: |
إضافة وسم
لا توجد وسوم, كن أول من يضع وسما على هذه التسجيلة!
|
| المؤسسة: | Chiang Mai University |
| الملخص: | Nonlinear current-voltage properties of zinc oxide-bismuth oxide varistors doped with cobalt oxide were investigated. The composition of ZnO doped with 0.5 mol% Bi2O3and 0.75 mol%CoO was prepared and sintered in two different surroundings, zinc oxide-bismuth oxide-cobalt oxide powder and alumina powder. Microstructures and element tracing were studied using scanning electron microscopy with X-ray microanalysis, electron probe microanalysis and X-ray diffraction. Results clearly showed that the alumina surrounding led to bismuth loss from the green body and degraded the nonlinear property of varistors. At sintering temperatures higher than 1150°C, the alumina-surrounding sintered specimens became ohmic and the electrical resistivity of 200 Ω cm was found in the specimen sintered at 1200°C. © 2004 Elsevier B.V. All rights reserved. |
|---|