Phase development and dielectric responses in PMN-BNT ceramics
(1 - x)Pb(Mg1/3Nb2/3)O3-x(Bi0.5Na0.5)TiO3 ceramics were prepared by the conventional mixed-oxide method. All compositions show complete perovskite solid solutions and the structure to change from cubic to rhombohedral at x = 0.5. The dielectric constant and dielectric loss tangent were measured as a...
Saved in:
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
2014
|
| Online Access: | http://www.scopus.com/inward/record.url?eid=2-s2.0-77950518458&partnerID=40&md5=b72b5ecf920e6c229359dba82630e7c7 http://cmuir.cmu.ac.th/handle/6653943832/6278 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Institution: | Chiang Mai University |
| Language: | English |
| Summary: | (1 - x)Pb(Mg1/3Nb2/3)O3-x(Bi0.5Na0.5)TiO3 ceramics were prepared by the conventional mixed-oxide method. All compositions show complete perovskite solid solutions and the structure to change from cubic to rhombohedral at x = 0.5. The dielectric constant and dielectric loss tangent were measured as a function of both temperature and frequency. The results indicated a relaxor ferroelectric behavior for all ceramics. The temperature at maximum of the dielectric constant of PMN-BNT ceramics were seen to increase with increasing BNT content. Moreover, the broadest dielectric peak occurs at x = 0.9, which leads to a morphotropic phase boundary in this system. © 2010 Elsevier Ltd and Techna Group S.r.l. |
|---|