Novel FeVO <inf>4</inf> /Bi <inf>7</inf> O <inf>9</inf> I <inf>3</inf> nanocomposite with enhanced photocatalytic dye degradation and photoelectrochemical properties
© 2018 Elsevier B.V. Novel FeVO 4 /Bi 7 O 9 I 3 nanocomposites with different weight percentages (3, 6.25, 12.5, and 25%wt) of FeVO 4 were successfully synthesized by cyclic microwave irradiation, followed by wet impregnation. The applications for photocatalytic dye degradation and photoelectrochem...
Saved in:
| Main Authors: | , , , , |
|---|---|
| Format: | Journal |
| Published: |
2019
|
| Subjects: | |
| Online Access: | https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=85059241166&origin=inward http://cmuir.cmu.ac.th/jspui/handle/6653943832/63673 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Institution: | Chiang Mai University |
| Summary: | © 2018 Elsevier B.V. Novel FeVO 4 /Bi 7 O 9 I 3 nanocomposites with different weight percentages (3, 6.25, 12.5, and 25%wt) of FeVO 4 were successfully synthesized by cyclic microwave irradiation, followed by wet impregnation. The applications for photocatalytic dye degradation and photoelectrochemical (PEC) were investigated. The 6.25%wt-FeVO 4 /Bi 7 O 9 I 3 nanocomposite exhibited excellent photocatalytic degradation of methylene blue, rhodamine B, and methyl orange with decolorization efficiencies of 81.3%, 98.9%, and 94.9% within 360 min, respectively. Moreover, this nanocomposite possessed excellent reusability and stability during the photocatalytic degradation process. PEC performance in water oxidation of the 6.25%wt-FeVO 4 /Bi 7 O 9 I 3 photoanode was evaluated by linear sweep voltammetry (LSV) measurement. Enhanced PEC performance with photocurrent density of 0.029 mA cm −2 at 1.23 V (vs. RHE) was observed under visible-light irradiation, which was ca. 3.7 times higher than that of the pure Bi 7 O 9 I 3 . Based on the optical characterization, energy band positions, and active species trapping experiments, a possible photocatalytic mechanism of the FeVO 4 /Bi 7 O 9 I 3 heterojunction was discussed. The enhancement in the photocatalytic and the PEC performance ascribed to synergistic effects of visible-light absorption and a favorable “type II heterojunction” structure of the FeVO 4 /Bi 7 O 9 I 3 nanocomposite. These were the main effects that promoted the photogenerated electrons and holes transfer across the contact interface between FeVO 4 and Bi 7 O 9 I 3 , as well as suppressed the recombination of photogenerated electron-hole pairs and facilitated charge separation and transportation. |
|---|