Synthesis, structural and electrical properties of double perovskite Sr2NiMoO6 ceramics

The double perovskite Sr2NiMoO6 powders and ceramics were prepared by two different (conventional and precursor) solid-state reaction methods. The phase structure was characterized by XRD and TEM techniques. It has been indicated that single-phase perovskite powders were obtained when calcined in ai...

Full description

Saved in:
Bibliographic Details
Main Authors: Prasatkhetragarn A., Kaowphong S., Yimnirun R.
Format: Article
Language:English
Published: 2014
Online Access:http://www.scopus.com/inward/record.url?eid=2-s2.0-83755172290&partnerID=40&md5=b85a5b748caaee6fbcb18d4712f46fe0
http://cmuir.cmu.ac.th/handle/6653943832/6390
Tags: Add Tag
No Tags, Be the first to tag this record!
Institution: Chiang Mai University
Language: English
Description
Summary:The double perovskite Sr2NiMoO6 powders and ceramics were prepared by two different (conventional and precursor) solid-state reaction methods. The phase structure was characterized by XRD and TEM techniques. It has been indicated that single-phase perovskite powders were obtained when calcined in air at 1300°C. However, nano-particles of the size 30-60 nm have been found in powders prepared with the precursor method, while those from the conventional route exhibit large irregular shaped particles with aggregation. The dielectric properties (εr and tan δ) were also examined in the sintered ceramics. The results showed the transition point at 280°C for conventional route, while no clear phase change was observed in ceramics from the precursor route. These observations clearly indicate that the different starting processes affected the phase formation behavior and the electrical properties of Sr2NiMoO6 ceramics. © 2011 Springer-Verlag.