Phase evolution and dielectric properties of barium zirconate titanate - Barium iron niobate ceramics
The structural and dielectric properties of (1-x)BaZr0.9Ti 0.1O3 (BZT) - xBaFe0.5Nb0.5O 3 (BFN) ceramics system were investigated as a function of the BaFe0.5Nb0.5O3 content by X-ray diffraction (XRD) and dielectric measurement technique. Studies were performed on the samples prepared by solid state...
Saved in:
| Main Authors: | , , , , |
|---|---|
| 格式: | Conference or Workshop Item |
| 語言: | English |
| 出版: |
2014
|
| 在線閱讀: | http://www.scopus.com/inward/record.url?eid=2-s2.0-79960736880&partnerID=40&md5=6065172b372082e4e966c6d33c39d5ac http://cmuir.cmu.ac.th/handle/6653943832/6493 |
| 標簽: |
添加標簽
沒有標簽, 成為第一個標記此記錄!
|
| 機構: | Chiang Mai University |
| 語言: | English |
| 總結: | The structural and dielectric properties of (1-x)BaZr0.9Ti 0.1O3 (BZT) - xBaFe0.5Nb0.5O 3 (BFN) ceramics system were investigated as a function of the BaFe0.5Nb0.5O3 content by X-ray diffraction (XRD) and dielectric measurement technique. Studies were performed on the samples prepared by solid state reaction for x = 0.2, 0.4, 0.6 and 0.8. Maximum density of the ceramic was obtained at 1450°C for every mixing conditions. The evolution of the tetragonal phase, indicating phase transition from cubic to tetragonal with increasing with BFN ratio. Lattice parameters were found to decrease with the BFN content. The dielectric properties of (1-x)BZT - xBFN ceramics were studied. It was found that the dielectric constant and broadness of their peak of these ceramics increased with increasing BFN contents, with the dielectric loss measured at 1 kHz was shown lower than 2.00 at working temperature ranging from room temperature to 400°C. Copyright © Taylor & Francis Group, LLC. |
|---|