Fabrication and characterization of porous bioceramic made from bovine bone powder mixed calcium phosphate glass
© 2019 Trans Tech Publications Ltd, Switzerland. Bovine bone xenograft was selected bioactive material currently widespread acceptable for using as human bone void filler. In this paper we described a new porous bioceramic block fabricated from bovine bone powders mixed with calcium phosphate glass....
Saved in:
| Main Authors: | , , , , , |
|---|---|
| Format: | Book Series |
| Published: |
2019
|
| Subjects: | |
| Online Access: | https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=85071602355&origin=inward http://cmuir.cmu.ac.th/jspui/handle/6653943832/66670 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Institution: | Chiang Mai University |
| Summary: | © 2019 Trans Tech Publications Ltd, Switzerland. Bovine bone xenograft was selected bioactive material currently widespread acceptable for using as human bone void filler. In this paper we described a new porous bioceramic block fabricated from bovine bone powders mixed with calcium phosphate glass. The characterized methods were atomic absorption spectrometer, x-ray diffraction, scanning electron microscope, energy dispersion x-ray spectroscopy, diffusion test, bending test, compressive test and Archimedes' principle. The final products showed interconnecting pores size range 100 to 500 μm, apparent porosity about 52% and mole ratio of Ca:P as 1.65. The toxic elements such as arsenic, cadmium, mercury, and lead were lower standard limits of ASTM I (American Society for Testing and Materials International). The samples had a compressive strength more than 400 kg/cm2. So, this object can be useful as an alternative choice for human bone substitute in the vertical compression load bearing area. |
|---|