Characterization and photonic absorption of hierarchical tree-like CdS nanostructure synthesized by solvothermal method
Hierarchical tree-like wurtzite CdS nanostructure was successfully synthesized by the 200°C and 24 h solvothermal reaction of cadmium nitrate and thiourea as starting materials in 1:1 volume ratio of diethylenetriamine and ethylenediamine as a mixed solvent. Phase and morphology of the as-synthesize...
Saved in:
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
2014
|
| Online Access: | http://www.scopus.com/inward/record.url?eid=2-s2.0-84861581819&partnerID=40&md5=817bf887f86bb5d9b1b95304d106b84d http://cmuir.cmu.ac.th/handle/6653943832/6740 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Institution: | Chiang Mai University |
| Language: | English |
| Summary: | Hierarchical tree-like wurtzite CdS nanostructure was successfully synthesized by the 200°C and 24 h solvothermal reaction of cadmium nitrate and thiourea as starting materials in 1:1 volume ratio of diethylenetriamine and ethylenediamine as a mixed solvent. Phase and morphology of the as-synthesized CdS product were characterized by X-ray diffraction (XRD), Raman spectroscopy and transmission electron microscopy (TEM), including its photonic absorption by UV-visible spectroscopy. XRD spectrum and TEM image showed hexagonal wurtzite CdS structure with a 1-2 μm prototypical cluster, composed of a number of limbed nanorods. Its Raman spectrum was specified as the first-order (1LO) and second-order (2LO) longitudinal optical phonon modes at 298 and 599 cm - 1. UV-visible spectrum shows an absorption peak centered at around 489 nm, assigned as the excitonic transition, blue shifted comparing to its bulk. © 2012 Elsevier B.V. All rights reserved. |
|---|