Improvement in dielectric and mechanical performance of CaCu 3.1Ti 4O 12.1 by addition of AL 2O 3 nanoparticles
The properties of CaCu 3.1Ti 4O 12.1 [CC3.1TO] ceramics with the addition of Al 2O 3 nanoparticles, prepared via a solid-state reaction technique, were investigated. The nanoparticle additive was found to inhibit grain growth with the average grain size decreasing from approximately 7.5 μm for CC3.1...
Saved in:
| Main Authors: | , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
2014
|
| Online Access: | http://www.scopus.com/inward/record.url?eid=2-s2.0-84856025754&partnerID=40&md5=8cc27a17a108b776c5b41cc849293a2b http://cmuir.cmu.ac.th/handle/6653943832/6865 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Institution: | Chiang Mai University |
| Language: | English |
| Summary: | The properties of CaCu 3.1Ti 4O 12.1 [CC3.1TO] ceramics with the addition of Al 2O 3 nanoparticles, prepared via a solid-state reaction technique, were investigated. The nanoparticle additive was found to inhibit grain growth with the average grain size decreasing from approximately 7.5 μm for CC3.1TO to approximately 2.0 μm for the unmodified samples, while the Knoop hardness value was found to improve with a maximum value of 9.8 GPa for the 1 vol.% Al 2O 3 sample. A very high dielectric constant > 60,000 with a low loss tangent (approximately 0.09) was observed for the 0.5 vol.% Al 2O 3 sample at 1 kHz and at room temperature. These data suggest that nanocomposites have a great potential for dielectric applications. © 2012 Puchmark and Rujijanagul. |
|---|