Influence of carbon nanotubes in gel electrolyte on photovoltaic performance of ZnO dye-sensitized solar cells
In this work, the poly(ethylene glycol) (PEG) gel polymer electrolyte was used to replace the liquid electrolyte in dye-sensitized solar cells (DSSCs) in order to overcome the issues of evaporation, leak of liquid, and stability. However, the PEG gel polymer electrolyte-ZnO based cells have low curr...
Saved in:
Main Authors: | , , , , , |
---|---|
Format: | Article |
Language: | English |
Published: |
2014
|
Online Access: | http://www.scopus.com/inward/record.url?eid=2-s2.0-84879232266&partnerID=40&md5=7394d7af7d53ef7127aebff17e206906 http://cmuir.cmu.ac.th/handle/6653943832/7074 |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Institution: | Chiang Mai University |
Language: | English |
Summary: | In this work, the poly(ethylene glycol) (PEG) gel polymer electrolyte was used to replace the liquid electrolyte in dye-sensitized solar cells (DSSCs) in order to overcome the issues of evaporation, leak of liquid, and stability. However, the PEG gel polymer electrolyte-ZnO based cells have low current density and fill factor. Then, the effect of addition of multi-walled carbon nanotubes (MWCNTs) in different wt% into the PEG gel polymer electrolyte was also investigated. Current density-voltage characteristics and electrochemical impedance spectroscopy showed that use of the MWCNTs with the PEG gel polymer electrolyte increases current density and fill factor. Highest efficiency of 0.75% was achieved with 5 wt% of the MWCNTs in the PEG gel polymer electrolyte. The enhancement of efficiency can be attributed to the suppression of charge transfer resistance at the ZnO photoelectrode/electrolyte interface, whereas the proper introduction of MWCNTs effectively decreases the charge recombination as confirmed by electrochemical impedance spectra. In case of stability, the devices sustained for 1006 h also maintained over 85% of its initial performance. © 2013 Elsevier Ltd. All rights reserved. |
---|