Compressive strength and microstructure of 0-3 lead zirconate titanate ceramic-portland cement composites
Lead zirconate titanate (PZT)-Portland cement (PC) composites have been reported to have good potential for use in smart structures. In this work, PZT-PC composites containing 40%, 50% and 60% of PZT by volume were produced and their mechanical and hydration properties were investigated. Compressive...
Saved in:
| Main Authors: | , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
2014
|
| Online Access: | http://www.scopus.com/inward/record.url?eid=2-s2.0-84891807688&partnerID=40&md5=ce6bba584699a0c54c8ad53efb0095f2 http://cmuir.cmu.ac.th/handle/6653943832/7321 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Institution: | Chiang Mai University |
| Language: | English |
| Summary: | Lead zirconate titanate (PZT)-Portland cement (PC) composites have been reported to have good potential for use in smart structures. In this work, PZT-PC composites containing 40%, 50% and 60% of PZT by volume were produced and their mechanical and hydration properties were investigated. Compressive strengths of those typically used in normal concrete were found for all PZT-PC composites, with measured values of 41.5-45.0 MPa. Hydration products of Portland cement detected by thermal analysis were calcium silicate hydrates (the main cement hydration product), calcium hydroxide and ettringite. Furthermore, calcium silicate hydrates and ettringite can also be observed surrounding the PZT grains in the SEM micrograph. © 2013 Copyright Taylor and Francis Group, LLC. |
|---|