PRA - RANCANGAN PRODUKSI SINGLE LAYER OIL PALM TRUNK TERIMPREGNASI EKSTRAK KAYU SURIAN (TOONA SINENSI) DAN RESIN PINUS (PINUS MERKUSII) : SIFAT FISIS DAN MEKANIS BATANG SAWIT (ELAEIS GUINEENSIS JACQ) TERIMPREGNASI RESIN PINUS (PINUS MERKUSII), SERBUK DAN EKSTRAK KAYU SURIAN (TOONA SINENSIS)
Oil palm trunk has the potential as a substitute material for wood, however, they have low physical and mechanical properties. One of the efforts to increase oil palm trunk with impregnation technology. Impregnation is a process of inserting a mixture of other compounds (filler) into the material (i...
Saved in:
| Main Author: | |
|---|---|
| Format: | Final Project |
| Language: | Indonesia |
| Online Access: | https://digilib.itb.ac.id/gdl/view/50494 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Institution: | Institut Teknologi Bandung |
| Language: | Indonesia |
| Summary: | Oil palm trunk has the potential as a substitute material for wood, however, they have low physical and mechanical properties. One of the efforts to increase oil palm trunk with impregnation technology. Impregnation is a process of inserting a mixture of other compounds (filler) into the material (in this case wood) to improve quality (Cai et al, 2018). This research was conducted to determine the optimum concentration of oil palm trunk impregnated with tusam resin, sawdust and surian extract on the physical and mechanical properties of wood. The research method used is the experimental method of impregnation technology using 2 (two) different impregnants, a mixture of surian extract and resin and a mixture of resin and surian sawdust. There were 4 variations of the impregnant concentration used for each treatmentsurian extract with resin 0%, 4%, 6%, 8% and resin with surian sawdust 0%, 4%, 6%, 8%. Each treatment was carried out 3 replications. The experimental design used was a completely randomized design (CRD) using DMRT analysis. The parameters observed included Polymer Loading (PL), density, Anti Swelling Efficiency (ASE), Water Absorption (WA), Modulus of Elasticity (MOE), Modulus of Rupture (MOR) and Tensile Strength. (TS). Based on the results of research, impregnation treatment with extracts of surian and resin 4% shows the optimum concentration with PL 65.52%, density 0.36 g / cm3, WA 65.32%, MOE 20.526.27 kgf / cm2, MOR 259.36 kgf / cm2 and TS 98.48 kgf / cm2. Impregnation treatment with resin and 0% surian sawdust showed the optimum concentration with PL 73.09%, density 0.51 g / cm3, WA 60.8%, MOE 12.332.40 kgf / cm2, MOR 133.5 kgf / cm2 and TS 71.65 kgf / cm2.
|
|---|