Study of fabrication Al-Tin slag composite by powder metallurgy method

• Main Author: Muhamad Syazwan Abdul Manan
• Other Authors: Mohd Fitri Mohamad Wahid (Advisor)
• Format: Learning Object
• Language: English
• Published: Universiti Malaysia Perlis 2008
• Subjects: Aluminum; Aluminum composites; Aluminum > Mechanical properties; Powder metallurgy; Tin slag; Aluminum matrix composite
• Online Access: http://dspace.unimap.edu.my/xmlui/handle/123456789/3350
• Institution: Universiti Malaysia Perlis

In the present investigation, Aluminum-tin slag composite have been produced by powder metallurgy (P/M) route. Aluminum (Al) and tin slag were undergo milling and sieving process where particle size <75 µm and <63 µm for tin slag and aluminum were obtained. Both Al and tin slag were mixed for 40 minutes with a speed of 100rpm. Both of the Al and tin slag powder were mixed by weight percent which is Al-5% of tin slag, Al-10% of tin slag, Al-15% of tin slag and Al-20% of tin slag correspond to sample A, B, C, D respectively. Samples were compacted with the load of 5 tonne (180 Mpa) for 3 minutes. The samples were placed in a tube furnace with nitrogen, N2 purified atmosphere at 600oC for 7 hours soaking time, with heating and cooling rate of 5oC/ min for 1 hour and 9 minutes respectively. Mechanical properties like shrinkage, hardness, density and porosity of Al-tin slag composite were investigated. All the samples experienced shrinkage. In increase addition of tin slag, hardness and density value was also increased. % of porosity decreased with the increased addition of tin slag. Microstructures of Al-tin slag composite were also investigated. The microstructure of this Al-tin slag composite shows a uniform distribution of tin slag in the Al matrix.