Intermetallic growth of SAC237 solder paste reinforced with MWCNT
The formation of intermetallic compound (IMC) layer at the interfaces of pad finishes has been studied. The growth of IMC layer as a reflow process and its properties were also discussed. In this study, solder alloy SAC237 (Sn: 99 wt.%, Ag: 0.3 wt.%, Cu: 0.7 wt.%), reinforced with 0.01 wt.% Multi-Wa...
Saved in:
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Universiti Putra Malaysia Press
2017
|
| Online Access: | http://psasir.upm.edu.my/id/eprint/58326/1/16%20JST%28S%29-0284-2017-2ndProof.pdf http://psasir.upm.edu.my/id/eprint/58326/ http://www.pertanika.upm.edu.my/Pertanika%20PAPERS/JST%20Vol.%2025%20(4)%20Oct.%202017/16%20JST(S)-0284-2017-2ndProof.pdf |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Institution: | Universiti Putra Malaysia |
| Language: | English |
| Summary: | The formation of intermetallic compound (IMC) layer at the interfaces of pad finishes has been studied. The growth of IMC layer as a reflow process and its properties were also discussed. In this study, solder alloy SAC237 (Sn: 99 wt.%, Ag: 0.3 wt.%, Cu: 0.7 wt.%), reinforced with 0.01 wt.% Multi-Walled Carbon Nanotubes (MWCNTs), was mixed to form a composite solder paste and soldered on Electroless Nickel Immersion Gold (ENIG) and Immersion Tin (ImSn) pad finishes. Reflow process was conducted in oven with specific reflow profile. The growth and properties of IMC layer were analysed using optical microscope with image analyser. Results showed that the thickness of IMC layer for ENIG and ImSn were 1.49 and 2.51 µm, respectively. Floating IMC and voids within the solder bulk and IMC layer were also identified in the samples. In addition, the measured wetting angle for ENIG and ImSn were 16.21° and 34.32°, respectively. |
|---|