A comparative study on the characteristics of mercury (Hg) doped BSCCO superconductors
Mercury (Hg)-doped BSCCO superconductors were prepared using a modified solid-state reaction method. X-ray diffraction analysis revealed the co-existence of the high-Tc and low-Tc phases in all the samples. The sample with the most number of high-Tc peaks had the nominal composition Hg0.4Bi2.0Sr2.0C...
Saved in:
Main Authors: | , |
---|---|
Format: | text |
Language: | English |
Published: |
Animo Repository
1997
|
Subjects: | |
Online Access: | https://animorepository.dlsu.edu.ph/etd_bachelors/4013 |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Institution: | De La Salle University |
Language: | English |
id |
oai:animorepository.dlsu.edu.ph:etd_bachelors-4875 |
---|---|
record_format |
eprints |
spelling |
oai:animorepository.dlsu.edu.ph:etd_bachelors-48752021-02-01T01:33:45Z A comparative study on the characteristics of mercury (Hg) doped BSCCO superconductors Chong, Wilson Florentin, Hanzel Mercury (Hg)-doped BSCCO superconductors were prepared using a modified solid-state reaction method. X-ray diffraction analysis revealed the co-existence of the high-Tc and low-Tc phases in all the samples. The sample with the most number of high-Tc peaks had the nominal composition Hg0.4Bi2.0Sr2.0Ca2.0Cu3.0Oy. This sample was annealed at 850 centigrade for 72 hours. Electrical resistivity measurement of this sample showed a two-step resistive transition. Zero resistivity was attained at 105K. The resistivity versus temperature graphs of the samples confirmed the presence of the high-Tc and low-Tc phases. 1997-01-01T08:00:00Z text https://animorepository.dlsu.edu.ph/etd_bachelors/4013 Bachelor's Theses English Animo Repository High temperature superconductors Superconductors Copper oxide superconductors Physics |
institution |
De La Salle University |
building |
De La Salle University Library |
continent |
Asia |
country |
Philippines Philippines |
content_provider |
De La Salle University Library |
collection |
DLSU Institutional Repository |
language |
English |
topic |
High temperature superconductors Superconductors Copper oxide superconductors Physics |
spellingShingle |
High temperature superconductors Superconductors Copper oxide superconductors Physics Chong, Wilson Florentin, Hanzel A comparative study on the characteristics of mercury (Hg) doped BSCCO superconductors |
description |
Mercury (Hg)-doped BSCCO superconductors were prepared using a modified solid-state reaction method. X-ray diffraction analysis revealed the co-existence of the high-Tc and low-Tc phases in all the samples. The sample with the most number of high-Tc peaks had the nominal composition Hg0.4Bi2.0Sr2.0Ca2.0Cu3.0Oy. This sample was annealed at 850 centigrade for 72 hours. Electrical resistivity measurement of this sample showed a two-step resistive transition. Zero resistivity was attained at 105K. The resistivity versus temperature graphs of the samples confirmed the presence of the high-Tc and low-Tc phases. |
format |
text |
author |
Chong, Wilson Florentin, Hanzel |
author_facet |
Chong, Wilson Florentin, Hanzel |
author_sort |
Chong, Wilson |
title |
A comparative study on the characteristics of mercury (Hg) doped BSCCO superconductors |
title_short |
A comparative study on the characteristics of mercury (Hg) doped BSCCO superconductors |
title_full |
A comparative study on the characteristics of mercury (Hg) doped BSCCO superconductors |
title_fullStr |
A comparative study on the characteristics of mercury (Hg) doped BSCCO superconductors |
title_full_unstemmed |
A comparative study on the characteristics of mercury (Hg) doped BSCCO superconductors |
title_sort |
comparative study on the characteristics of mercury (hg) doped bscco superconductors |
publisher |
Animo Repository |
publishDate |
1997 |
url |
https://animorepository.dlsu.edu.ph/etd_bachelors/4013 |
_version_ |
1712576164558536704 |