High thermoelectric performance in supersaturated solid solutions and nanostructured n-type PbTe–GeTe

Sb-doped and GeTe-alloyed n-type thermoelectric materials that show an excellent figure of merit ZT in the intermediate temperature range (400–800 K) are reported. The synergistic effect of favorable changes to the band structure resulting in high Seebeck coefficient and enhanced phonon scattering b...

Full description

Saved in:
Bibliographic Details
Main Authors: Luo, Zhong-Zhen, Zhang, Xiaomi, Hua, Xia, Tan, Gangjian, Bailey, Trevor P., Xu, Jianwei, Uher, Ctirad, Wolverton, Chris, Dravid, Vinayak P., Yan, Qingyu, Kanatzidis, Mercouri G.
Other Authors: School of Materials Science & Engineering
Format: Article
Language:English
Published: 2020
Subjects:
Online Access:https://hdl.handle.net/10356/140250
Tags: Add Tag
No Tags, Be the first to tag this record!
Institution: Nanyang Technological University
Language: English
Description
Summary:Sb-doped and GeTe-alloyed n-type thermoelectric materials that show an excellent figure of merit ZT in the intermediate temperature range (400–800 K) are reported. The synergistic effect of favorable changes to the band structure resulting in high Seebeck coefficient and enhanced phonon scattering by point defects and nanoscale precipitates resulting in reduction of thermal conductivity are demonstrated. The samples can be tuned as single-phase solid solution (SS) or two-phase system with nanoscale precipitates (Nano) based on the annealing processes. The GeTe alloying results in band structure modification by widening the bandgap and increasing the density-of-states effective mass of PbTe, resulting in significantly enhanced Seebeck coefficients. The nanoscale precipitates can improve the power factor in the low temperature range and further reduce the lattice thermal conductivity (κlat). Specifically, the Seebeck coefficient of Pb0.988Sb0.012Te–13%GeTe–Nano approaches −280 µV K−1 at 673 K with a low κlat of 0.56 W m−1 K−1 at 573 K. Consequently, a peak ZT value of 1.38 is achieved at 623 K. Moreover, a high average ZTavg value of ≈1.04 is obtained in the temperature range from 300 to 773 K for n-type Pb0.988Sb0.012Te–13%GeTe–Nano.