Microstructure and erosion-corrosion behaviour of as-cast high chromium white irons containing molybdenum in aqueous sulfuric-acid slurry

• Main Authors: S. Imurai, Ch Thanachayanont, J. T.H. Pearce, T. Chairuangsri
• Format: Journal
• Published: 2018
• Subjects: Agricultural and Biological Sciences
• Online Access: https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=84958207318&origin=inward; http://cmuir.cmu.ac.th/jspui/handle/6653943832/44772
• Institution: Chiang Mai University

Microstructure and erosion-corrosion behaviour of as-cast high chromium white irons containing molybdenum in aqueous sulfuric-acid slurry was studied. The experimental irons contained 28 wt.%Cr with a Cr:C ratio of about 10 and up to 10 wt.%Mo. The irons with up to 6 wt.%Mo are hypoeutectic, whereas the iron with 10 wt.%Mo becomes eutectic/peritectic. Mo addition promotes formation of M 23 C 6 and M 6 C, instead of typical M 7 C 3 . Erosion-corrosion testing was performed in aqueous sulfuric-acid slurry containing alumina particles. The hypoeutectic Fe-28Cr-2.7C-1Mo with mainly M 7 C 3 and the eutectic/peritectic Fe-28Cr-2.6C-10Mo showed reduced wear rates of about 30% and 7% of that of the reference iron without Mo addition, respectively. The reduction of the carbide-matrix hardness difference, the increase of corrosion resistance of the matrices, and the increase of macro-hardness are determining factors for the improvement of erosion-corrosion resistance of the irons.