Fabrication of glass foams from industrial wastes used as insulating board
Insulating glass foam (IGF) was successfully fabricated by wet process. The starting proportion of 65 wt% waste glass, 12 wt% slag, 23 wt% commercial soap was added with 15 wt% Na2SiO3 and represented then was sintered at 725 °C. The IGF had cellular structure with the macro-pore size at 0.428 mm an...
Saved in:
| Main Authors: | , , , |
|---|---|
| 格式: | Book Series |
| 出版: |
2018
|
| 主題: | |
| 在線閱讀: | https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=84884950255&origin=inward http://cmuir.cmu.ac.th/jspui/handle/6653943832/52540 |
| 標簽: |
添加標簽
沒有標簽, 成為第一個標記此記錄!
|
| 總結: | Insulating glass foam (IGF) was successfully fabricated by wet process. The starting proportion of 65 wt% waste glass, 12 wt% slag, 23 wt% commercial soap was added with 15 wt% Na2SiO3 and represented then was sintered at 725 °C. The IGF had cellular structure with the macro-pore size at 0.428 mm and thin cell walls. Density, thermal conductivity and compressive strength were 0.310 g/cm3, 0.130 W/m.K and 0.78 MPa, respectively. The average pore diameter and porosity increased with increasing the Na2SiO3 concentration and the sintering temperature. On the other hand, the density, thermal conductivity and compressive strength were decreased. © (2013) Trans Tech Publications, Switzerland. |
|---|