Microstructure and erosion-corrosion behaviour of as-cast high chromium white irons containing molybdenum in aqueous sulfuric-acid slurry

• المؤلفون الرئيسيون: S. Imurai, Ch Thanachayanont, J. T.H. Pearce, T. Chairuangsri
• التنسيق: دورية
• منشور في: 2018
• الموضوعات: Materials Science
• الوصول للمادة أونلاين: https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=84958207318&origin=inward; http://cmuir.cmu.ac.th/jspui/handle/6653943832/54620
• المؤسسة: Chiang Mai University

Microstructure and erosion-corrosion behaviour of as-cast high chromium white irons containing molybdenum in aqueous sulfuric-acid slurry was studied. The experimental irons contained 28 wt.%Cr with a Cr:C ratio of about 10 and up to 10 wt.%Mo. The irons with up to 6 wt.%Mo are hypoeutectic, whereas...