Dielectric properties of PZT-PCN ceramics under compressive stress
In this study, ceramics in PZT-PCN systems with a formula (1-x)Pb(Zr 1/2 Ti1/2) O3-(x)Pb(Co1/3Nb 2/3)O3 (x=0.1-0.5) were prepared by a solid-state mixed-oxide technique. The phase formation and microstructure were studied using x-ray diffraction (XRD) and scanning electron microscopy (SEM), respecti...
محفوظ في:
| المؤلفون الرئيسيون: | , , , , |
|---|---|
| التنسيق: | مقال |
| اللغة: | English |
| منشور في: |
2014
|
| الوصول للمادة أونلاين: | http://www.scopus.com/inward/record.url?eid=2-s2.0-43249131523&partnerID=40&md5=2f0af638195d3d8785f267d044d7f10c http://cmuir.cmu.ac.th/handle/6653943832/5593 |
| الوسوم: |
إضافة وسم
لا توجد وسوم, كن أول من يضع وسما على هذه التسجيلة!
|
| المؤسسة: | Chiang Mai University |
| اللغة: | English |
| الملخص: | In this study, ceramics in PZT-PCN systems with a formula (1-x)Pb(Zr 1/2 Ti1/2) O3-(x)Pb(Co1/3Nb 2/3)O3 (x=0.1-0.5) were prepared by a solid-state mixed-oxide technique. The phase formation and microstructure were studied using x-ray diffraction (XRD) and scanning electron microscopy (SEM), respectively. Effects of compressive stress on the dielectric properties of PZT-PCN ceramics were investigated at stress up to 230 MPa using a compressometer. The results clearly showed that the dielectric constant of the PZT-PCN ceramics increased significantly with increasing applied stress, while the dielectric loss tangent showed an opposing trend. The experimental observations have been attributed to a combination of the domain switching and the deaging mechanisms from the application of the compressive stress. © 2008 The Royal Swedish Academy of Sciences. |
|---|