Dielectric properties of liquid phase sintered 0.98BaTiO<inf>3</inf>-0.02Ba(Mg<inf>1/3</inf>Nb<inf>2/3</inf>)O<inf>3</inf>ceramic
The sintering temperature of 0.98BaTiO3-0.02Ba(Mg1/3Nb2/3)O3(BT)(BMN) ceramics was lowered from around 1300 to 900 °C through liquid phase sintering to obtain various microstructural and dielectric properties. The linear shrinkage and densities were recorded and their microstructures were investigat...
محفوظ في:
المؤلفون الرئيسيون: | A. Munpakdee, J. Tontrakoon, K. Siriwitayakorn, T. Tunkasiri |
---|---|
التنسيق: | دورية |
منشور في: |
2018
|
الموضوعات: | |
الوصول للمادة أونلاين: | https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=25444509832&origin=inward http://cmuir.cmu.ac.th/jspui/handle/6653943832/62212 |
الوسوم: |
إضافة وسم
لا توجد وسوم, كن أول من يضع وسما على هذه التسجيلة!
|
المؤسسة: | Chiang Mai University |
مواد مشابهة
-
Compositional range and electrical properties of lead-free Bi<inf>0.5</inf>(Na<inf>0.8</inf>K<inf>0.2</inf>)<inf>0.5</inf>TiO<inf>3</inf>-(Ba<inf>0.98</inf>Nd<inf>0.02</inf>) TiO<inf>3</inf>system
بواسطة: P. Jaita, وآخرون
منشور في: (2018) -
Effect of composition on electrical properties of lead-free Bi<inf>0.5</inf>(Na<inf>0.80</inf>K<inf>0.20</inf>)<inf>0.5</inf>TiO<inf>3</inf>-(Ba<inf>0.98</inf>Nd<inf>0.02</inf>)TiO<inf>3</inf>piezoelectric ceramics
بواسطة: Pharatree Jaita, وآخرون
منشور في: (2018) -
Compositional range and electrical properties of lead-free Bi<inf>0.5</inf>(Na<inf>0.8</inf>K<inf>0.2</inf>)<inf>0.5</inf>TiO<inf>3</inf>-(Ba<inf>0.98</inf>Nd<inf>0.02</inf>) TiO<inf>3</inf>system
بواسطة: P. Jaita, وآخرون
منشور في: (2018) -
Effect of composition on electrical properties of lead-free Bi<inf>0.5</inf>(Na<inf>0.80</inf>K<inf>0.20</inf>)<inf>0.5</inf>TiO<inf>3</inf>-(Ba<inf>0.98</inf>Nd<inf>0.02</inf>)TiO<inf>3</inf>piezoelectric ceramics
بواسطة: Pharatree Jaita, وآخرون
منشور في: (2018) -
Phase evolutions and electrical properties in BaTiO<inf>3</inf>-BaFe<inf>0.5</inf>Nb<inf>0.5</inf>O<inf>3</inf>ceramics
بواسطة: U. Intatha, وآخرون
منشور في: (2018)