Effects of filtered cathodic vacuum arc deposition (FCVAD) conditions on photovoltaic TiO2 films
Titanium dioxide (TiO2) films for photovoltaic applications were synthesized using filtered cathodic vacuum arc deposition (FCVAD) technique. Various deposition conditions were tested for an optimal film formation. The conditions included the oxygen (O2) pressure which was varied from a base pressur...
Saved in:
| Main Authors: | , , , , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Elsevier
2014
|
| Online Access: | http://www.scopus.com/inward/record.url?eid=2-s2.0-84903309650&partnerID=40&md5=6130c4ef285a9c35e5e50f91a6557f74 http://cmuir.cmu.ac.th/handle/6653943832/7332 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Institution: | Chiang Mai University |
| Language: | English |
| Summary: | Titanium dioxide (TiO2) films for photovoltaic applications were synthesized using filtered cathodic vacuum arc deposition (FCVAD) technique. Various deposition conditions were tested for an optimal film formation. The conditions included the oxygen (O2) pressure which was varied from a base pressure 10-5 to 10-4, 10-3, 10 -2 and 10-1 Torr, sample holder bias varied using 0 or -250 V, deposition time varied from 10, 20 to 30 min, and deposition distance varied from 1 to 3 cm. The deposited films were also annealed and compared with unannealed ones. The films under various conditions were characterized using optical microscopy, scanning electron microscopy (SEM), atomic force microscopy (AFM), energy-dispersive X-ray spectroscopy (EDS) and Raman spectroscopy techniques. The film transparency increased and thickness decreased to a nanoscale with increasing of the O2 pressure. The transparent deposited films contained stoichiometric titanium and oxygen under the medium O2 pressure. The as-deposited films were TiO2 containing some rutile but no anatase which needed annealing to form. © 2014 Elsevier B.V. |
|---|