Effect of brushing on surface roughness, fluoride release, and biofilm formation with different tooth-colored materials
Background/purpose: Tooth brushing, material mechanical ageing procedure, is the most effective way in removing biofilm. The purpose of this study was to investigate the surface roughness, fluoride-release, and S. mutans biofilm formation on various tooth-colored restorative materials before and aft...
Saved in:
| Main Author: | |
|---|---|
| Other Authors: | |
| Format: | Article |
| Published: |
2023
|
| Subjects: | |
| Online Access: | https://repository.li.mahidol.ac.th/handle/123456789/84484 |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Institution: | Mahidol University |
| Summary: | Background/purpose: Tooth brushing, material mechanical ageing procedure, is the most effective way in removing biofilm. The purpose of this study was to investigate the surface roughness, fluoride-release, and S. mutans biofilm formation on various tooth-colored restorative materials before and after brushing. Materials and methods: Discs of materials, a nanocomposite (Filtek Z350XT; CO), a giomer (Beautifil II; GIOMER), a resin-modified glass-ionomer material (Fuji II LC; RMGI), and a conventional glass-ionomer material (Fuji IX GP Extra; GI), were prepared, polished with abrasive discs (SofLex), and divided into brushed and not brushed groups. The surface roughness of specimens was observed using a contact profilometer, fluoride-release was measured using a fluoride-specific ion electrode, and S. mutans biofilm formation, biovolume and live/dead cells, was observed under a confocal laser scanning microscope. Results: Higher roughness was observed on GI and RMGI than on CO and GIOMER. Brushing had no effect on the roughness. The fluoride-release of GI and RMGI was higher than that of GIOMER. The fluoride-release decreased after brushing in all materials. The biovolume of S. mutans was not significantly different between GIOMER, RMGI and GI, while CO showed the highest. Brushing resulted in a higher biovolume for all materials, except CO, which showed no change. After brushing, all the tested materials demonstrated identical biovolumes. There were no significant differences in live/dead cells among all groups. Conclusion: Brushing demonstrated a negative effect on the fluoride-release and biovolume of S. mutans biofilms for all tested materials except nanocomposites. |
|---|