Silicide formation from laser thermal processing of Ti/Co bilayers

Silicide formation from laser thermal processing of Ti/Co bilayers

A bilayered CoTi silicide structure consisting of an amorphous CoTi silicide and a highly textured CoTi silicide was found after pulsed excimer laser annealing of titanium/cobalt/silicon stack at high fluence of 0.6 J/cm2. The highly textured CoTi silicide is monocrysta...

Full description

Saved in:
Bibliographic Details
Main Authors: Chow, F. L., Pey, Kin Leong, Lee, Pooi See, Tung, Chih Hang, Wang, X. C., Lim, G. C., Chong, Y. F.
Other Authors: School of Materials Science & Engineering
Format: Article
Language:English
Published: 2012
Subjects:
DRNTU::Engineering::Materials::Microelectronics and semiconductor materials
Online Access:https://hdl.handle.net/10356/94699
http://hdl.handle.net/10220/8094
Tags: Add Tag
No Tags, Be the first to tag this record!
Institution: Nanyang Technological University
Language: English
Description
Summary:A bilayered CoTi silicide structure consisting of an amorphous CoTi silicide and a highly textured CoTi silicide was found after pulsed excimer laser annealing of titanium/cobalt/silicon stack at high fluence of 0.6 J/cm2. The highly textured CoTi silicide is monocrystalline and fully coherent with the Si(111) plane of the substrate but has a large amount of microstructural defects. The constitutional supercooling phenomenon is the solidification mechanism responsible for the highly textured CoTi silicide. The incomplete crystallization shown by the presence of the amorphous CoTi silicide is attributed to a high concentration of titanium impurity.

Similar Items